PolyTerra PolyTerra PLA is a bioplastic 3D printing filament in which organic materials have been combined with PLA to reduce the plastic content and develop a more environmentally friendly filament. PLA PolyTerra prints just like PLA, so no print settings need to be changed and the...

€19³⁴

Χωρίς ΦΠΑ: €15.60

Σε Απόθεμα

+ −

Παράδοση

— ELTA Courier
— ACS Courier
— ΓΕΝΙΚΗ ΤΑΧΥΔΡΟΜΙΚΗ

Τρόποι πληρωμής

Περιγραφή
Χαρακτηριστικά
Skroutz Αξιολογήσεις

PolyTerra

PolyTerra PLA is a bioplastic 3D printing filament in which organic materials have been combined with PLA to reduce the plastic content and develop a more environmentally friendly filament.

PLA

PolyTerra prints just like PLA, so no print settings need to be changed and the overhang and bridging functions can even outperform PLA. With a wide printing temperature range from 190 to 230 ° C, PolyTerra can be processed on any extrusion-based 3D printer.

Recommended Settings

Nozzle temperature: 190 – 230 ℃
Build plate temperature: 25 - 60 ˚C
Printing speed: 30-70 mm/s
Build Surface material: BuildTak® , Glass, Blue Tape
Cooling Fan: ON

Basic Data
Filament Typ	PLA
Diameter	1,75 mm
Tolerance	-
Weight	1,00 kg
Lenght	317 m
Color	Brown
Color	-

Printing Parameter
Recomended Printing Temp Min	190 ºC
Recomended Printing Temp Max	230 ºC
Recomended Printbed Temperature Min	25 ºC
Recomended Printbed Temperature Max	60 ºC
Recomended Printing Speed Min	30 mm/s
Recommended Printing Speed Max	70 mm/s
Recomended Fan Speed Min	-
Recomended Fan Speed Max	100 >#/td###
Recomended Retraction Min	1 mm
Recomended Retraction Max	-
Recomended Flow Rate Min	-
Recomended Flow Rate Max	-

General
Specific gravity	1,31 g/cm3 ISO 1183
Mold Shrinkage	-
Specific volume resistivity	-

Temperature
Vicat softening temp	62,7 °C ISO 306
Heat deflection temp	-

Tensile
Tensile strength	-
Tensile modulus	-

Elongation
Elongation at yield	-
Elongation at break	34,5 % ISO 527

Flexural
Flexural Strenght	39,6 % ISO 178
Flexural Modulus	2695 ISO 178

Other
Impact Strenght Unnotched	-
Impact Strength	5,7 KJ/m2 ISO 179