Αρχική/3D PRINTERS/CNC/3D FILAMENTS & RESINS/PRIMACREATOR VALUE FLEX UV RESIN - 500 ML - CLEAR

PRIMACREATOR VALUE FLEX UV RESIN - 500 ML - CLEAR

Κωδικός Κατασκευαστή (MPN): PV-RF-B405-0500-CL

ΚΩΔΙΚΟΣ: AA2452

MANUFACTURERPRIMACREATOR MPNPV-RF-B405-0500-CL

Main advantages of PrimaCreator Value Flex Resin: Shore hardness of 65-75 D & elongation at break of 130% 3D print high detail results that needs to have a very high impact strength 3D print flexible objects with very small shrinkage Optimized for UV Lightsource 395 – 405 nm. Performs...

€45¹⁴

Χωρίς ΦΠΑ: €36.40

Σε Απόθεμα

+ −

Παράδοση

— ELTA Courier
— ACS Courier
— ΓΕΝΙΚΗ ΤΑΧΥΔΡΟΜΙΚΗ

Τρόποι πληρωμής

Περιγραφή
Χαρακτηριστικά
Skroutz Αξιολογήσεις

Main advantages of PrimaCreator Value Flex Resin:

Shore hardness of 65-75 D & elongation at break of 130%
3D print high detail results that needs to have a very high impact strength
3D print flexible objects with very small shrinkage
Optimized for UV Lightsource 395 – 405 nm.
Performs well on low powered DLP 3D printers
Fast curing time, 4 - 12 (depending on color) seconds per layer – for quicker prints

Cleaning of PrimaValue Flex 3D prints

After printing, clean your 3D print in IPA (Isopropyl Alcohol) to rinse off resin left on the model.

Curing the finished & washed 3D prints

When it´s time for curing you can use sunlight or a uv curing chamber.Depending on print the curing times can vary: In a UV light curing chamber, it will take about 2-5 minutes. In sunlight, 10-20 minutes. In daylight on a cloudy day, it can take up to 60 minutes.

Flexural modulus	1.882 - 2.385 MPa
Flexural strength	40-70 MPa
Hot deformation temp.	80 ℃
Thermal expansion	95*E-6
Volume shrinkage	3.72 - 4.24%
Linear shrinkage	1.05 - 1.35%
Tensile strength	30 - 52 MPa
Tensile modulus	1.779 - 2.385 MPa
Elongation at break	130%
Hardness (Shore D)	65 - 75D
Glass transition temp.	100 ℃
Density	1.05-1.25g/cm3
Notched impact strength	41-48 j/m
Viscosity	150-300 MPa·s
Curing time	4 - 12s for layer thickness 0.05 mm Bottom layer 40 - 60 s

Προβλήθηκαν Πρόσφατα